Extending the temperature range of the Cmcm phase of SnSe for high thermoelectric performance
- Tian Gao
- Yi Wen
- Shulin Bai
- Lizhong Su
- Haonan Shi
- Rong Liu
- Sining Wang
- Yixuan Hu
- Shibo Liu
- Dongrui Liu
- Shan Liu
- Chao Liang
- Xiaokun Feng
- Xiaoqian Wang
- Yongxin Qin
- Xiang Gao
- Bingchao Qin
- Cheng Chang
- Peikang Bai
- Li-Dong Zhao
2025-12-18
Thermoelectric power generation requires high dimensionless figure of merit ZT across broad temperatures. The two-dimensional phonon and three-dimensional charge transports enable n-type– Pnma tin selenide (SnSe) crystals to show a peak ZT of ~3.0 at 748 kelvin. In this work, we focused on the high-symmetry Cmcm phase to boost two-dimensional phonon and three-dimensional charge transports and extended the high-performance ( ZT ~ 3.0) plateau. By simultaneously broadening the Cmcm -phase stability window and enhancing lattice symmetry through lead alloying, we extended the high performance from a single temperature point to a wide temperature range of ~250 kelvin in rock salt–like Cmcm SnSe crystals rendered n-type through chlorine doping. An average ZT of ~3.0 was achieved between 673 and 923 kelvin, with a conversion efficiency of ~19.1% under a temperature difference of ~572 kelvin.