Flexible metal-organic framework films for reversible low-pressure carbon capture and release
- Sumea Klokic
- Benedetta Marmiroli
- Giovanni Birarda
- Florian Lackner
- Paul Holzer
- Barbara Sartori
- Behnaz Abbasgholi-NA
- Simone Dal Zilio
- Rupert Kargl
- Karin Stana Kleinschek
- Chiaramaria Stani
- Lisa Vaccari
- Heinz Amenitsch
2025-08-04
Transitioning metal-organic frameworks (MOFs) from laboratory-scale to carbon dioxide (CO 2 ) capture and storage applications (CCS) requires in-depth understanding of their adsorption properties and structural stability, especially for film assemblies. However, evaluating their performance is challenging, particularly under low or moderate CO 2 pressure conditions, which are key for cost and performance efficiency. Herein, we explore the low-pressure CO 2 uptake and release within flexible Zn-based MOF film structures with diverse ligand functionalities, employing quartz crystal microbalance, synchrotron radiation-based infrared spectromicroscopy and grazing incidence wide-angle X-ray scattering measurements. To investigate CO 2 adsorption and its interaction with Zn-MOF pores, we exploited the framework’s flexibility by triggering structural changes and thus variations of the pore-environment using two stimuli, temperature and light. Results show considerable promise for stimuli-induced on-demand CO 2 capture and release at low pressures, demonstrating structural reversibility under near-ambient conditions and highlighting the potential of tailored MOF film structures in advancing green CCS-technologies.